Zirlux® Anterior Multi

Zirlux® Anterior Multi

Multi-Layered Zirconia with more indications and strength than Lithium Disilicate.

Zirlux Anterior Multi is a multilayered Zirconia with fully gradient shading that matches the Incisal, Dentin, and Gingiva of dentition—making it suitable for anterior restorations. The transition of layers mimics the translucency and esthetics of a natural tooth without adding the necessary steps to the workflow. Zirlux Anterior Multi can be characterized after sintering for cases that require additional customization.

  • Axially pressed Zirconia followed by cold isostatic pressing using even pressure from every direction creates consistency and ensures the finest quality.
  • Each disc is quality checked before final packaging to ensure the material is of the highest quality.
  • Compatible with Roland, Amann Girrbach, and most open 98.5mm CAD/CAM Milling Machines.

Indications

  • Full Contour Crowns
  • 2-3 Unit Bridges
  • Telescopic Crowns
  • Veneers

Order Now

Physical Characteristics

Density before sintering

≥6.0 g/cm3

CTE after sintering (25-500°C)

(10.5 ± 1.0) x10 -6K-1

3-point flexural strength after sintering

600 Mpa

Accelerated aging surface monoclinic phase content

<5%

Chemical solubility after sintering

<100ug/cm2

Cytotoxicity test

0 level

Radioactivity after sintering

<0.1Bq/g

Sintering temperature

1430~1470°C
1450°C recommended

Chemical Composition

ZrO2 + HfO2

86.3%~94.2%

Y2O3

5.8%-9.7%

Er2O3

<2%

Fe2O3

<0.5%

AI2O3

<0.5%

Other Oxides

<0.5%